Aquavox Latex 403X
TWO-COMPONENT WATERPROOFING FLEXIBLE MORTAR

BARCODE ITEM NO TYPE
643845887674 WU7674 A-50 Lb.
643845887674 WU7674 B-2.11 Galls

AQUAVOX LATEX 403X TWO-COMPONENT, FLEXIBLE WATERPROOFING MORTAR

Two-Component
Waterproof
Full Flexible
Waterproofing
• Terraces
• Pools
• Balconies
• Suitable For Water Tanks
• Emulsion Polymer Based
• Resistant To De-Icing Salts, Sulphates,
Chlorides & Carbon Dioxide

Highly flexible waterproofing compound of cement based powder component and polymer emulsion based liquid component, which is fit for use in drinking water tanks and which can be applied prior to the top coating material.

AQUAVOX LATEX 403X is applied for waterproofing:
•Waterproofing of swimming pools, bathrooms, showers, balconies, terraces or before laying ceramic tiles.
•Waterproofing of concrete basins of potable water.
•Waterproofing of underground concrete elements like foundations, retaining walls, basement walls.
•Waterproofing of places subject to deformation, pedestrian and load traffic.
•Waterproofing of concrete basins subject to sea water and de-icing salts.

Product Advantages
Suitable for contact drinking water
Non-corrosive for steel and construction elements
Applicable both on horizontal and vertical surfaces
Resistant to freeze-thaw
Water repellant nature
Fully elastic
Protection of concrete surfaces which may come into contact with seawater, de-icing salts, such as sodium or calcium chloride, and sulphates.

Limitations
The product should not be applied against negative water pressure
The product should, once mixed, be used before the expiration of its pot life
Any foreign material should not be added into the product’s components of the product during the application.
The surface should be preserved from air currents and water contact during and after the application.
The product should not be applied to such surfaces, which are exposed to risk of freezing within the next 24 hours, which are frozen or the frost of which is thawing.
Due care should be given to prevent the exposure of the material to direct sunlight in hot weather conditions.
Application should be held at temperatures between 5°C-35°C
The surface and ambient temperature should be between +5°C and +35°C whilst at application.

Useful time for prepared mixture – Pot life Maximum 3 hours
Stand by period between coats Minimum 6 hours
Required standby time before subsequent application Minimum 3 days
Property Typical Results
Density 1,50 kg /dm3
Initial adhesion strength ≥ 0,5 N/mm2
Adhesion strength after water contact ≥ 0,5 N/mm2
Adhesion strength after thermal ageing ≥ 0,5 N/mm2
Adhesion strength after freezing – thawing cycles ≥ 0,5 N/mm2
Adhesion strength after hard water contact ≥ 0,5 N/mm2
Waterproofing No Penetration, ≤ 20 gr

Coverage
18 M2 PER MM OF THICKNESS / 190 SQFT PER 1/32” THICKNESS