Aquavox Latex Uv 405X
TWO-COMPONENT UV RESISTANT WATERPROOF MORTAR
AQUAVOX LATEX UV 405X AQUAVOX LATEX UV 405X TWO-COMPONENT UV RESISTANT WATERPROOF MORTAR
AQUAVOX LATEX UV 405X is high quality White cement based, polymer emulsioned, high flexible and UV Resistant waterproofing mortar.
Resistant To UV RaysWaterproofHigh FlexibilityWaterproofing In Coastal Areas Terraces & Pools & BalconiesSuitable For Water TanksResistant To De-Icing Salts, Sulphates Resistant To Chlorides & Carbon DioxideWater Repellant Nature
Highly flexible waterproofing compound of cement based powder component and polymer emulsion based liquid component, which is fit for use in drinking water tanks and which can be applied prior to the top coating material.
AQUAVOX LATEX UV 405X is applied for waterproofing:
•Protects against UV Rays•Suitable for contact drinking water•Waterproofing bathrooms, showers, balconies, terraces, swimming pools etc. before laying ceramic tiles •Waterproofing of concrete basins of potable water•Waterproofing plasterboard, render or cementitious surfaces, lightweight cement blocks and marine-grade plywood •Waterproofing hydraulic channels, faces of dams and basins •Waterproofing of underground concrete elements like foundations, retaining walls, basement walls•Protection of cementitious renders or concrete with cracks, against infiltration of water and aggressive elements from the atmosphere
•Flexible protection layer of new concrete structures
•Flexible protection layer repaired structures
•Waterproofing of concrete basins subject to sea water and de-icing salts
•Non-corrosive for steel and construction elements
•Protection of concrete surfaces which may come into contact with seawater, de-icing salts, such as sodium or calcium chloride, and sulphates
Suitable for contact drinking water
Non-corrosive for steel and construction elements
Applicable both on horizontal and vertical surfaces
Resistant to freeze-thaw
Water repellant nature & Fully elastic
Protection of concrete surfaces which may come into contact with seawater, de-icing salts, such as sodium or calcium chloride, and sulphates.
The product should not be applied against negative water pressure
The product should, once mixed, be used before the expiration of its pot life
Any foreign material should not be added into the product’s components of the product during the application
The surface should be preserved from air currents and water contact during and after the application.
The product should not be applied to such surfaces, which are exposed to risk of freezing within the next 24 hours, which are frozen or the frost of which is thawing.
Due care should be given to prevent the exposure of the material to direct sunlight in hot weather conditions.
Application should be held at temperatures between 5°C-35°C
|Useful time for prepared mixture – Pot life||Maximum 3 hours|
|Stand by period between coats||Minimum 6 hours|
|Required standby time before subsequent application||Minimum 3 days|
|Density||Approximately 1,50 kg /dm3|
|Initial adhesion strength||≥ 0,5 N/mm2|
|Adhesion strength after water contact||≥ 0,5 N/mm2|
|Adhesion strength after thermal ageing||≥ 0,5 N/mm2|
|Adhesion strength after freezing – thawing cycles||≥ 0,5 N/mm2|
|Adhesion strength after hard water contact||≥ 0,5 N/mm2|
|Waterproofing||No Penetration, ≤ 20 gr|
18 M2 PER MM OF THICKNESS / 190 SQFT PER 1/32” THICKNESS